1.Kimik konpozisyon
Kalite | C (max) | Mn (max) | P (max) | C (max) | Si (max) | Cr (max) | Ni (max) | Mo | Lòt |
304 | 0.08 | 2.0 | 0.045 | 0.03 | 1.0 | 18-20 | 8-12 | - | |
304L | 0.03 | 2.0 | 0.045 | 0.03 | 1.0 | 18-20 | 8-12 | - | |
316 | 0.08 | 2.0 | 0.045 | 0.03 | 1.0 | 16-18 | 10-14 | 2-3 | - |
316L | 0.08 | 2.0 | 0.045 | 0.03 | 1.0 | 16-18 | 10-14 | 2-3 | - |
2.Mechanical Properties
Kalite | Uts | Sede | Pwolonjman | Dite | Nimewo DIN KONN | |
N / mm2 | N / mm2 | % | HRB | Wroyght | Mete | |
304 | 600 | 210 | 60 | 80 | 1.4301 | 1.4308 |
304L | 530 | 200 | 50 | 70 | 1.4306 | 1.4552 |
316 | 560 | 210 | 60 | 78 | 1.4401 | 1.4408 |
316L | 530 | 200 | 50 | 75 | 1.4406 | 1.4581 |
3. Rezistans korozyon chimik
Anjeneral pale, 304 asye pur ak 316 asye pur gen ti kras diferans nan chimik rezistans korozyon, men yo diferan nan kèk medya espesifik.
Okòmansman devlope Nerjaveèi asye 304 se pi plis sansib a kowozyon nan pwen pwen nan kondisyon espesifik. Ajoute 2-3% MOLYBDENUM ka diminye sansiblite sa a, ki rezilta yo nan 316. Anplis de sa, sa yo MOLYBDENUM kapab tou redwi korozyon a nan kèk asid thermoorganic.
4.Low Kabòn Nerjaveèi asye
Se rezistans a korozyon nan asye enustenitik asosye ak kouch la oksid CHROMIUM pwoteksyon ki te fòme sou sifas metal la. Si se materyèl la chofe a 450 00 -900 ℃, estrikti a nan materyèl la pral chanje ak CHROMIUM karbur pral fòme sou kwen an kristal. Kidonk, kouch pwoteksyon nan oksid CHROMIUM pa kapab fòme nan kwen nan kristal la, ki mennen nan diminye nan rezistans korozyon.
Se konsa, asye pur 304L ak 316L asye pur yo te devlope reziste sa a korozyon. Kontni an kabòn nan asye pur 304L ak 316L asye pur yo pi ba, paske se kontni an kabòn redwi, kidonk pa pwal gen okenn CHAMTIUM carbure.